1. Ingredient List
Si |
AI |
Ca |
Mn |
Cr |
P |
S |
C |
|
FeSi75A10.5-A |
74-80 |
0.5 |
1 |
0.4 |
0.3 |
0.035 |
0.2 |
0.1 |
FeSi75A10.5-B |
72-80 |
0.5 |
1 |
0.5 |
0.5 |
0.04 |
0.2 |
0.2 |
FeSi75A11.0-A |
74-80 |
1 |
1 |
0.4 |
0.3 |
0.035 |
0.2 |
0.1 |
FeSi75A11.0-B |
72-80 |
1 |
1 |
0.5 |
0.5 |
0.04 |
0.2 |
0.2 |
FeSi75A11.5-A |
74-80 |
1.5 |
1 |
0.4 |
0.3 |
0.035 |
0.2 |
0.1 |
FeSi75A11.5-B |
72-80 |
1.5 |
1 |
0.5 |
0.5 |
0.04 |
0.2 |
0.2 |
FeSi75A12.0-A |
74-80 |
2 |
1 |
0.4 |
0.3 |
0.035 |
0.2 |
0.1 |
FeSi75A12.0-B |
74-80 |
2 |
1 |
0.4 |
0.3 |
0.04 |
0.2 |
0.1 |
FeSi75A12.0-C |
72-80 |
2 |
0.5 |
0.5 |
0.04 |
0.2 |
0.2 |
|
FeSi75-A |
74-80 |
0.4 |
0.3 |
0.035 |
0.2 |
0.1 |
||
FeSi75-B |
74-80 |
0.4 |
0.3 |
0.04 |
0.2 |
0.1 |
||
FeSi75-C |
72-80 |
0.5 |
0.5 |
0.04 |
0.2 |
0.2 |
||
FeSi65 |
65-72 |
0.6 |
0.5 |
0.04 |
0.2 |
|||
FeSi45 |
40-70 |
0.7 |
0.5 |
0.04 |
0.2 |
2.Related introduction
A. Low silicon iron can replace some ferrosilicon alloys to deoxidize and increase silicon, increase iron, effectively control the temperature of molten steel, and do not affect the absorption rate of other alloys during use;
B. Low-silicon molten iron can reduce the amount of ore and scrap steel, and ensure the normal healing rate of the molten pool metal. In this way, it can realize steelmaking with less slag, reduce lime consumption and increase metal recovery;
3.Product production
4. Quality control
5. Support sea ,land and air transportation
6. Support express delivery
http://www.glory-metallurgy.com/